Main Composition
+Unsaturated polyester resin, peroxide, filing.
Application
●Fast fixing, pattern making, repairing and bonding for stone, granite and various stones, etc.
Main Properties
• Double components adhesives; • Short curing time (the exact time depending on application temperature;
• High hardness could be polished after curing; • Wide range of operation (-10°C\~45°C);
● Various colors for allkinds of stone color, such as transparent, cream, white, black, red, green, etc @ Hardener is white gel.
Physical Characteristics of Part A (adhesive)
B
| ResinType | Unsaturated polyesterresin | Main Composition | Organic peroxide | |||
| Shape | Transparent pasty | trar yeleisiguid | Colored pasty | Colored semlliquid | Shape | white gel |
| Viscosity (25°C)* | 100000- 300000 C.P | 700-1200 C.P | 350,000 800,000 C.P | 4000- 80000 C.P | Visoosity | 100,000-200,000 C.P |
| Density | 1.05-1.15g/cma | 1.05-1.15g/cm³ | 1.5-1.7g/cma | 1.4-1.6g/cma | Density | 1.12-1.18g/cm† |
| Shelf life | 12 months in original package, reserved in cooland ventilate place. | storage | 1tiie | |||
Instruction
• Make the surfaoe dry, clean and slighly rough;
• Mix adhesive with hardener according to the ratio 100:3 and stir them fullyuntl the mixture achieve uniformed color;
• Paint the slate surfaoe with the mixing tool, such as scraper;
• Refer to the application direction on the package before using.
Attention
• Do not return the mixed glue to the original package ● Add more or less hardener to the adhesive to make the curing time shorter or longer;
• Stored in dry and shady plaoe and keep the lid tighty dosed after using;
+ Do not make the bonded parts exposed in wet and frosty place;
• Refer to the application direction on the package before using.
Packing
| 1L/TIN | 3L/ TIN | 4L/TIN | 20L/ TIN |
| 12TIN/CTN | 4TIN/CTN | 4TIN /CTN |
● 12 months of shel life (reler to the manufacture date printed on the lid);
● Clean the tools immediately with acetone after using;
@ If to bond the hanging parts, please use our epoxy AB Adhesive;
Main Composition
Epoxy resin, organic modified amine, quartz powder.
Application
• The dry bonding of hanging parts for intemal or exlermal stone wall.
• Reinforcing or bonding of the precast concrete or structure frame.
• Bonding or pattem making for the tiles and marbles.
• Fissure filling for concrete. · Joint for tiles, brick and concrete, etc. • Anchor adhesive. • Not available for smooth surface.
• Not available for stone surfaoe finished care prooessing.
• Not available for working in water or oil surlace.
Main Properties
• Fine aging resistance, strong tenacity, water-proof and moisture-proof after curing, Chemical resistance, weather resistance(-10-90°C).
• High thickness adhesive with no liquid dropping and high utilization ratio.
● Fine quake-resistance, super shock resistance, high compression strength and tensile strength, etc.
● No corrosion. Harmless to human body. Clean operating environment, Iow construction cost, reducing the process of lime and sand transport and
• the expense of silt displacement.
Typical Physical Properties
| PartA | PartB | |||
| Resin type | Epoxy resin | Main ingredient | Organic modified amine | |
| Appearance | Gel in white color | Appearance | Gel in cream color | |
| Viscosity(25°C) | 10,000-30,000 .CP | Viscosity(25°C) | 10,000-30,000 C.P | |
| Density | 1.5-1.6g/cm3 | Density | 1.5-1.6g/cm3 | |
| Shelflife(10 -25°C) | 12 month in col plaoe | Shelf life(10 -25°C) | 12 month in cool place | |
| Dangerous oomposition | none | Dangerous composition | none | |
| Garbage discharge | Base on national laws and local provisions | Garbage discharge | Base on national laws and local provisions | |
| Item | Standard index | Tested data | Test standard |
| Working time (25'C)/ min. | 5-30 | 15 | GB/T12954-1991 |
| Working temperature/ *C | -10-40 | -10-40 | GB/T12954-1991 |
| Using temperature/ *C | -45-90 | -45-90 | GB/T12954-1991 |
| Impulsion intensity Kg/m2> | 3.0 | 4.5 | GB/T2571-1995 |
| Shear Strength /Mpa | 8.0 | 18.0 | GB/T7124-1996 |
| Impress strength/MPa(stone-stone) | 10.0 | 17.0 | JC 887-2001 |
| Impress strength/MPa(stone-steel) | 10.0 | 17.5 | JC887-2001 |
Attention
• Make the bonded surface rough. • Operating temperature: -10-45 4 5 • Do not move the bonded parts until it is solidified completely.
• Heat the adhesive to 30-40 c i used in winter.
• Do not operate in the wet place. Effective operating period for mixed adhesive is 15 minutes.
• Do not retum the mixed adhesive back to the cans.
• Clean the tools immediately with aoetone after using.
• Keep away from children to avoid eating mistakenly.
• Shel life:12 month (stored in dry and ventilate place), i the quality is unchanged after guarantee period, it also could be used.
• Please carefully read the operating instruction on the package before using.
Instruction
• Surface pretreatment: bonded surface must be clean, no laitance, no dirt, no loose mortair, no oil, etc.
• Mix A with B according to the ratio 1:1 and stir them full until the mixture achieve uniforrmed color.
• Paint the bonded surface evenly with the steel soraper or other tools like this.
Packing
| 2kg / set (A+B) | 10kg / sct (A+B) | 30kg / set (A+B) |
| 9 set/ Ctn | 1 set/ Ctn |
EpoxyadhesiveofStone
Direct Bonding Method
1.The installation height is less than 9 meters, and walling structural strength is better. 2.Hanging fixing for the headroom distance between slate and wal face is less than1 centimeter.
Direct Bonding Method for Steel Frame
1.The wal of loose material or the wal with pooer foundation strength. 2.Special molding for elevation or modification for cylinder.
Transitional Bonding Method
Anchor Transitional Bonding Method
Bonding points M in then 2 Mer ntene hole
Fx bending peints-ollng te midde hole aad dedusting-niing
heema hedeenigdppgac
er into tha alby glaher the oureg l nlonboek, roeng adhesive-guing-lng
1.The installation height is less than 9 meters, and walling structural strength is better. 2.Wall face is uneven; the headroom distance between wal face and slate is more than 1 centimeter.
1.The installation height is less than 9 meters, and walling structural strength is pooer. 2.Decoration and reconstruction for old wall or fixing for thinner synthetic stone slabs of big dimension.
1.Hanging parts on the high-rise exterior facing or bigger headroom distance between wall face and slate. 2.The wall of loose material or walling structural strength is lower.
STONEDRYHANGING STRUCTURALADHESIVE
Main Composition
• Epoxy resin, organic modified amine, quartz powder
Application
• Dry hanging bonding of various stone materials. Bonding, reinforcing, joint filling, repairing and sealing of reinforced concrete building structural parts.
Instruction
e Clean up the surlace to be bonded. Mix components A and B aocording to the ratio of 1:1, tum over and stir until completely uniform. Apply glue with a scraper or other tool.
Attention
• If the bonding surface is too smooth, please be sure to polish it. The dry hanging glue can’t bear the load at the initial stage of curing. • The effective construction time of the mixed colloid is within 15 minutes • Initial curing time is after mixing 30-60 minutes at 2 5 ^ { \circ } C _ { \circ } fully cured and reaching the corresponding strength after 24 hours, the storage period of AB glue in the original sealed package is one year, retest after one year, if the perlormance is qualilied, it can still be used .
Greenand environmentally friendlyformula
The raw materials do not add formaldehyde, benzene and other organic substances, which are green, environmentally friendly and harmless to health
SLATECOMPOSITE GLUE
Application
• Slate glue is a flowable two-component product, which endows the glue with weather resistanoe and high bond strength by modifying epoxy and acrylic resin, and is suitable for bonding slate and slate at a 45-degree angle. Composite use of plates and stainless steel, iron, wood, etc. This product is used to bond various comp osite material plates such as granite, quartz stone, and artificial marble.
Main Properties
• Due to its creamy consistency, it has good handling properties on both horizontal and vertical surfaces.
• Can be applied at low temperature (-10°C) • Strong adhesion, waiterproof and oiFproof;
• The curing speed is fast (8-12 minutes), which is conducive to mechanical construction.
Instruction
• Add-3ofsf,sC), coating on the board.
Attention
• Clean the tool immediately after using, scrape off the uncured adhesive or clean it with acetone;
• Safety measues ate workplace:Gloves,masks,protectivegasses andothritems mustbeavailble.Theworkplacemustbe keptvtlated
Whntheessieosi,seuyu immediately.
Storage
• Under the condition of avoiding light and cooling (25C), the validity period is 12 months.
Fast-Curing AB Adhesive
Main Composition
● Bisphenol A epoxy resin and unsaturated polyester resin.
Application -
• Bonding for stone and stone, wood, steel products, glass.
Main Properties
• Light-colored, itle tendency to yellow stain; • Can be operated at low temperatures (-30°C-45°C): • Cure in short time.
Instruction
• Make the surlace to be bonded dry and rough; • Mix the A with B according to the regulated ratio 100 : 2—3 til the uniform color achieved, paint the stone with inferior permeability 3 or 4 times to get a better bonding result; • Curing time of the mixed adhesive is 4\~10 minutes at 20°C(68°F); after 30\~60 minutes, it can be operated, such as bumishing, locking holes, cutting, etc.
Attention
• Do not reload the mixed adhesive back to the original packing;
• Keep the lid tightly closed after using;
Donotoches asinwiiecaseofisaio.adverettoesdshitanwaendakeessarymicae;
• 12 months valid if stored in ventilative place; could stil be used if retest shows to be qualified.
| 9kg/set | 15kg/set |
ModifiedEpoxyResin ABAdhesive
Main Composition
• Bisphenol A epoxy resin and unsaturated polyester resin.
Scope of application
• Bonding between stone and stone, wood, steel and glass.
Product characteristics
• The light yellow color tends to decrease.
• It can be constructed at low temperature (- 30\~45 C ).
• It has the characteristics of fast curing.
Production process
• Clean the surface to be bonded, or grind the smooth surface rough, the efect is better. • Glue mixing: evenly mix the two groups of glue according to the proportion of A: B= 100:2-3, and then evenly apply them on the bonding surface. For the stone with poor permeability, repealedly apply 3-4 times to avoid affecting the bonding effect. • After mixing, under the condition of 20 ^ \circ \mathbb { C } (68 ° F), the initial solidlification time is 4-10 minutes, and after 30-60 minutes, deep processing can be carried out, such as grinding. keying, cutting, etc
Note
• Please do not put the mixed glue back into the tank, and close the cover tightly after use.
• This productisiritating. Do notucheyes and skin.Incase ofcontact, washwith plentyofwater andtake necessry medicalmeasures.
• The shelf life is 12 months.
Silicone Weather-Proofing Sealant168
Product Characteristics
SAIERSHI 168 Neutral slicone weatherproof sealant (ketoxime type) can be bonded and sealed with most building mate rials andcurtain wallmaterials, such as glass, coated gass, aluminum, sprayed aluminum, ceramics, sanitary ware, concrete, stone,stel,stnless steel,etc; las godadeivenes, extesibility, watertitess andairtessforsealingthejints of automobiles, containers, relrigerators and lamps.
Usage Method
● It can be used directly without mixed catalyst or other raw materials;
@ It will not react with other materials and has no corrosivity;
e Excellent weather aging resistance. UV, ozone, rain, ice and snow and extreme high andlow temperature changes will not affct it.Aftersolidification,it can sillmaintain elasticity within the temperature of- 40C to+20o C, and wi not harden, soften and crack;
○ Environment-friendly materials, non-poluting, belong to non-hazardous goods transportation.
Construction Requirements
• The malerial surface lemperalure must be within the range of 6 \mathbb { C } - 50 c before construction;
• The material surface must be dry, dean and free of oil stain;
• Compatibility test must be done before use.
keep in storage
• Store in a cool and dry place with temperature below 27 C ; • Use within 10 months after the production date.
Note: Avoid exoessive inhalation ofvolatile gases during curing, Properventlation shallbe maintainedduring onstruction. First aid: Il you lelunwel, move to fresh air immediately. /symptoms persist, seek medical attention immediately. IMPORTANT: Can not be used for structural application or material surface temperature exceeds 50 C
Product Characteristics
e SAIERSHI168A slicone stone weatherproof sealant s mainly used for seaing the joints of dry-hanging stone curtain wall works and oement precast slab works, and also for sealingthe joints of oncrete works and ceramic works. It has excellent bonding and sealing effct on most building materials such as natural stone, artificial marble, glass, aluminum, stainless steel, concrete and ceramic.
Usage Method
● I can be used directly without mixed catalyst or other raw materials;
● No corrosivity to metal, coated glass, marble and other building materials;
e Excellent weather aging resistance, can resist te direct erosion of ultraviolet, ozone, rain, ice and snow, and can remain elastic within - 40 C to+2oo C after solidification, without hardening, softening or cracking;
e Environment-Iriendly materials, non-poluting, belong to non-hazardous goods transportation.
Construction Requirements
• The malerial surface lemperature must be within the range of 6 \boldsymbol { \Sigma } - 50 C before construction;
● The material surface must be dry, dean and free of oi stain;
• Compatibility test must be done before use.
keep in storage
Store in a cool and dry place with temperature below 27 C ; ● Use within 10 months after the production date.
Note: Avoid excessive inhalation ofvoletile gases during curing, Proper ventltionshallbe maintained during construction. First aid you feelunwel, move lo fresh air immediately. F symptoms persist, seek medical attention immediately. IMPORTANT: Can not be used for structural application or material surface temperature exceeds 50 C
Product Characteristics
• SAIERSHI 168S high-performanoe neutral silicone weatherproof sealant can be bonded and sealed with most building materials and curtain wallmaterials, such as glas, coated glass, aluminum, painted aluminum, ceramics, sanitary ware, concrete, stone, steel, stainless steel, etc;Itas good adheiveness, extensibilty, water tghtness, air tghtess andother properties for caulking and sealing of automobiles, containers, refrigerators and lamps.
Usage Method
✳ It can be used directly without mixing catalyst or other raw materials;
● It will not react with other materials and has no corrosivity;
• Exoellent weather aging resistance, UV, ozone, rain, ice and snow, and extreme high and low temperature changes wil not affect it. After solidification
e It can maintain elasticity from- 40 C to+20o C without hardening, cracking and fragmentation; Environment-friendly materials, non-polluting, belong to non-hazardous goods transportation.
Construction Requirements
● The material surfaoe temperature must be within the range of 6 C - 50 C before construction;
Φ The malerial surlace must be dry, cean and free of oil stain;
✳ Compatibility test must be done before use.
keep in storage
• Store in a cool and dry plaoe with temperature below 27 C ; ● Use within 10 months after the production date.
Note: Avoid exoessive inhaletion ofvoletle geses during curing, Properventltion shallbe maintained during constructin. First aid: I you feel unwel,move to fresh airimmediately.Ifsymptoms persist, seek mecdical atlention immediately. IMPORTANT: Can not be used for structural application or material surface temperature exceeds 50 C
Product Characteristics
● SAJERSH 268 silicone structural sealant is mainly used for bonding and sealing of glass curtain wal, aluminum plate curtain wall,stone curain wall,daylighting roof and metal structural assembly, and also forsecondary bonding and sealing of insulating glass and industrial sealing.
Usage Method
✳ It can be used directly without mixed catalyst or other raw materials;
+ No corrosivity to aluminum, steel, stone and other materials;
• Excellent resistance to clmate aging and direct erosion of UV, ozone, rain, ice and snow; High and low temperature resistance, excelent performance, can maintain elasticityinthe temperature of- 50 C to+150 C aer solidification, and wil not harden, soften and crack;
● Environment-friendly materials, non-polluting, belong to non-hazardous goods transportation,
Construction Requirements
● The material surface temperature must be within the range of 6 C - 50 C before construction;
• The material surface must be dry, cean and free of oil stain;
• Compatibility test must be done before use.
keep in storage
• Store in a cool and dry place with temperature below 27 C ; • Use within 10 months after the production date.
Note: Avoid excessive inhalation of volatile gases during curing, Proper ventlation shallbe maintained during construction.
First aid: Il you feel unwell, move to fresh air immediately, If symptoms persist, seek medical attention immediately,
Main Composition
Unsaturated polyester resin (yellwish), peroxide.
Application
Bonding, repairing, holes filling, and pattern making for stone and ceramics.
Main Properties
● Be operated at Iow temperatures;
• Fine polish-ablity;
• Cure in short time;
● High bonding strength.
Direction
● Make the surface to be bonded dry and clean, ● Mix A with B according to the regulated ratio 2: 5 till the uniform color achieved; ● Paint the surface to be bonded evenly with the mixture;
Attention
• Stored in oool and shady place;
+ Do not return the excess back to the original package;
● Keep the lid tightly closed;
④ Do not touch eyes and skin because of its Irritation. If touch with eye and skin carelessly, wa.sh with clean water immediately and take necessary medical measures;
● Shelf life:6 months stored in shady places. (Date of manulacture printed on the lid).
13 KG /Drum
20 KG/Drum
The package can be made into different specifications according to per customer's special requirement.
Planting baradhesive
Main Composition
● Polyurethane modified epoxy acrylate, peroxide, quartz powder.
Application
● Construction jointing, road widening, bridge strengthening, storehouse strengthening and old buildings redecoration, etc.
Main Properties
• Double Components Adhesives;
● Environment friendly;
● Water resistance, freeze-thaw resistance, acid and alkali resistance, aging resistance, heat resistance and fire resistanoe;
• Low sensitivity to humidity;
• Fine affinity with ooncrete equal effectiveness to embedded objects
Attention
● Continuous operating recommended to avoid waste;
• Do not operate in wet plaoe;
• Make sure the holes clean during operating;
• The operating temperature should be between -10°C\~40'C;
• The recommended dosage of the adhesive is 2/3 of the hole volume or fil the hole up;
• Fill the hole from the bottom to avoid bubbles;
● 12 months shelf Iife stored in ventilative place;
• Clean the tools immediately with acetone after using • Refer to the application direction on the package before using.
| 4L(4kg) plus 110g hardener;4 | 18L(20kg)/ Drum plus 1L(600g) |
| sets/ctn | hardener |
Injectable-type AnchorAdhesive
Main Composition
Φ This product is made of modified vinyl high-strength resin and nano-materials. I is a twocomponent rebar planting adhesive for new building structures, The product is applicable to the bonding of almost all building base materials and metal anchors, such as concrete, block, stone, etc. It has the advantages of fast curing, high strength, large anchoring force, high acid and alkali resistance, aging resistance, etc. It is an ideal choice for planting reinforcement, reinforcement and reconstruction, and installation engineering.
Product characteristics
@ Strong acid and alkali resistance, aging resistance, good heat resistance, no creep at roon temperature.
@ Low humidity sensitivity, stable long-term load in humid environment.
@ Fixed without expansion stress, small edge specing, and good seismic performanoe.
e It can anchor reinforcement of various sizes, and the effect is equivalent to embedded
reinforoement.
e Injection-type operation, without manual mixing, can shorten the oonstruction progress and save time.
@ Tube-type packaging, the unused glue in the tube can be reused without waste
Scope of application
@ Steel bar embedding and anchor bolt anchoring in various building structures.
@ Anchorage of various equipment foundations.
@Anchorage support for roof and wall of mine roadway.
@ Anchorage of water conservancy facilities, wharves, highways, bridges and other projects.
@ Installation and anchoring of curtain wall, chemical equipment, pipeline, billboard, etc.
Performance parameter
@Appearance: A (main agent): white putty B (curing agent): red or black putty
@ Mixture viscosity: 18-22pa. S
● Solids density: 1.5 ± 0.10g/cm
@ Blending (volume ratio): 5:1
@ Operation time and curing time
| Ambient temperatureC | -5 | 0 | 10 | 20 | >30 |
| Operational time (min) | 15 | 10 | 5 | 4 | 2 |
| Curing time (min) | 180 | 150 | 120 | 90 | 60 |
| Size d(mm) | Aperture D(mm) | Hole depth T(mm) | Glue Injection volume I(2/3V) | Theoretical glue number(root) | Remarks (buried depth) |
| M8 | 12 | 80 | 6.03 | 59.7 | 10d |
| M8 | 12 | 120 | 9.04 | 39.8 | 15d |
| M10 | 14 | 100 | 10.26 | 35.1 | 10d |
| M10 | 14 | 150 | 15.08 | 23.4 | 15d |
| M12 | 16 | 120 | 16.09 | 22.4 | 10d |
| M12 | 16 | 180 | 24.12 | 14.9 | 15d |
| M14 | 18 | 210 | 35.61 | 10.1 | 15d |
| M16 | 22 | 160 | 40.52 | 8.9 | 10d |
| M16 | 22 | 240 | 60.79 | 5.9 | 15d |
| M18 | 25 | 270 | 88.31 | 4.1 | 15d |
| M20 | 28 | 200 | 82.06 | 4.4 | 10d |
| M20 | 28 | 300 | 123.09 | 2.9 | 15d |
| M22 | 30 | 330 | 155.43 | 2.3 | 15d |
| M25 | 32 | 250 | 133.97 | 2.7 | 10d |
| M25 | 32 | 375 | 200.96 | 1.8 | 15d |
| Size d(mm) | 10 | 12 | 14 | 16 | 18 | 20 | 22 | 25 | 28 | 30 | 32 | 36 | 40 | |
| Borehole diameter (mm) | 14 | 18 | 20 | 22 | 25 | 28 | 30 | 32 | 35 | 37 | 40 | 42 | 48 | |
| Design value | Buried depth 10d | 19.5 | 27.7 | 36.2 | 50.1 | 61.5 | 81.1 | 98.2 | 125.2 | 155.3 | 190.8 | 199.1 | 237.6 | 245.4 |
| of fension | Bured 15d | 24.2 | 33.1 | 46.9 | 61.8 | 77.7 | 96.5 | 116.8 | 149.3 | 187.5 | 236.1 | 258.3 | 309.6 | 372.1 |
Usage method
Packaging, storage and transportation
@ 400ml/piece, 30 pieces/box, packed with plastic rigid tube.
e It should be stored in a cool, dry and ventilated warehouse with a storage period of 1 year.
e This product is non-toxic and non-hazardous, and is transported as general chemical building materials.
● If you accidentally touch the skin, please wipe it with acetone and then wash it with water.
Beauyification Filler
Product Introduction
• Selz seaming agent is a high-quality two-component environment-friendly seaming product, which is made of German technology and imporled highquality environment-friendly materials, advanced equipment and sophisticated technology. It is rich in color, bright as porcelain, and has exoellent properties such as mildew and bacleriostasis resistance, alkali and crack resistance, solid adhesion, pollution resistance and easy cleaning. It thoroughly solves the problems of dirty black and yellow, mildew and fungus, easy to stick and oil stain, and difficult to scrub in the ceramic tile gap and room corners.
• This product is a green environmental prolection producl, which takes care of the health of the beauticians and people.
Scope of application
• Beautiful seam mosaic of polished brick, glazed brick, archaize brick, fullbody brick, microcrystaline, jade crystal, mosaic and other walls, floor tiles or background wall; ● The kitchen bathroom includes the mildew-proof, waterproof and beautiful seam sealing at the cormers of the cabinets, vegetable basins, stoves, wash tables, bathrooms, bathtubs and dosets.
Transportation and storage
e During transportation, avoid inversion, extrusion, impact, freezing, sun exposure and rain, • The products shall be stored in a oool, dry and ventilated warehouse. • The appropriate temperature of the storage room is 5C\~35C.
Construction technology
• Before construction, carefuly clean the oil stains, loose matter and other pollutants on the construction brick surface and joints;
● During construction, the special booster glue gun must be used, the cap of the glue bottle must be unscrewed and loaded into the booster glue gun, and the glue shal be pumped to AB component and discharged at the same time;
● Installthe matching glue nozzle, press the glue gun, hit the glue 10 cm in front of the glue on the waste paper, and observe the color of the glue until there is no color diference and the glue does not disperse. At this time, start to align the gap and apply glue evenly;
● After gluing, use professional caulking ball(to be purchased separately) to pullfrom one end along the brick seam to the other end, and keep the forceUnilorm; Within 2-3 hours, use a knife or shovel to dean the residual materials on the ceramic tile surfaoe that are not completely cured; low temperatureThe cleaning time shall be exlended;
●If it is necessary to keep the sealant on the same level with the tile surface after curing, you can paste the masking paper on both sides of the tle,After gluing, use a scraper to smooth along the gap, leave it standing for 5-10 minutes, and tear off the Meiwen paper.
Never collapse, never fall off, never to shrink Durable waterproof, milldew, Hacking Hard as porcelain, bright colors
Germantechnologyand environmentalprotection materials
Hardas porcelain, bright in color
Antimildew,bacteriostasis, alkali and crack
StoneProtective Agent
Main Composition
● Organic silicon resin, strong penetrating agent.
Application
• Various granite, marble, limestone (such as flag slab,stone plate, stone carving, head stone, etc).
Properties
● With strong permeability, it can effectively penetrate into the stone to achieve the best protective effect, and does not change the color of the stone surfaoe without leaving any traces2, With excellent chemical resistance, aging resistance and weather resistance, walerproof, anti-pollution properties.
Direction
• Thoroughly dean the surfaoe of the stone and ensure the processing surface is dry and free of dust, oil and other pollutants.2, Use roller brush or sponge uniformly coating on the surface of the stone in dry oondition3, make it static Ior 10 minutes with a rag to erase the exoess residue.4, It wil takes more than 24 hours to let it dry naturally -
• Do not clean the surface before it dry totally.
● Depending on varieties of stone finishes or project needs a second processing to enhance the effect.5, the amount depending on the type of stones, smooth stone 10 m2 / L ,and 5m2 / L to the matte side.6, According to the real condition, please do test in small area: firstly, When confirm the dosage and achieve the ideal effect, then begin large area construction.7, Shel life is 24 months. (manufecturing date is printed on the lid or the bottom of pot)
| 4L/Drum | 20L/ Drum |
All-purpose ceramic tileadhesive
It is suitable for pasting various ceramic wall and floor tiles such as slate, ceramic tile, natural stone, etc.
This product has passed the test of National Chemical
Building Materials Test Center
Test basis:
JC887-2oo1 Epoxy Adhesive for Dry Hanging Stone
Curtain Wall
Summary
● SAlERSHl all-purpose ceramic tile adhesive is mainly used for pasting decorative materials such as ceramic tiles, faoe tiles, floor tiles, etc. It is widely used for the decoration of internal and external walls, floors. bathrooms, kitchens and other buildings. Its main characteristics are high bonding strength, water resistance, freeze-thaw resistance, good aging resistance and convenient construction, It is a very ideal bonding material.
Main components
• Methyl methacrylate vinegar, SBS modified resin.
Features and advantages
obviously improve the work efficiency and convenience. l service life of the ceramic tile. S
Usage method
rough before construction. Teopo
Note
● Al surfaces shallbe solid, clean, freefrom hollowing, oil stain, wax stain, release agent and other loose substances
• The painted surlace shal be roughened to expose at least 80% of the original surface
• After the concrete surface is completed, it shall be cured for at least 28 days before laying bricks;
• The newy plastered surlace shal be cured for at least 7 days before laying bricks;
eTeoloe after being dried for 24 hours;