江苏廣信感光新材料股份有限公司（股票代码：300537）成立于2006年，
2016年于深交所创业板上市。公司专注于光刻胶、光伏胶、涂料等光固化电子化
学品的研发、生产和销售，产品涵盖PCB光刻胶、光伏胶、显示光刻胶、半导体光
刻胶及消费电子涂料、汽车涂料、印铁、食品包装等专用涂料。作为高新技术企
业，公司拥有核心配方技术，配备先进实验室和资深研发团队，产品品质和研发能
力在行业内具有显著影响力。
Jiangsu Kuangshun Photosensitivity New-material Stock Co.,Ltd.(Stock Code:
300537), established in 2006 and listed on the Shenzhen Stock Exchange GEM in
2016. Kuangshun Material has been committed to the R&D, production, and sales
of various electronic chemicals in photocuring field, mainly for photoresists,photovoltaic and coatings. Its product range covers PCB photoresists, display photoresists, semiconductor photoresists, as well as specialized coatings for consumer
electronics, automotive applications, metal package, and food package. As a
high-tech enterprise, the company possesses core formulation technologies,
advanced laboratories, and a seasoned R&D team, with its product quality and
R&D capabilities holding significant influence in the industry.
公司介绍
ABOUT US
热固绝缘胶（绿色）
Heat curable insulation layer/（Green）
指标 Requirement 结果 Result
绝缘性
Insulation resistance ≥1×10 Ω
适合丝网印刷
For screen print
良好的印刷特性，塑形佳，宽泛的操作窗口
Good printing characteristics & shaping， wide processing window
优异的绝缘性、耐PCT性
Excellent insulation performance & PCT resistance
与胶膜粘接力强
High peel strength with encapsulation film
体积电阻
Volume resistivity ≥1×10 Ω.cm 13
击穿强度
Dielectric strength ≥15kV/mm
有机扩散
Organic spread ＜15%
有机浸润
Organic infiltration ＜200um
耐湿热性能
DH1000 pass
耐冷热冲击
TC200 pass
高压蒸煮试验
PCT 96hours
固化后硬度
Pencil hardness ≥5H
高温后翘曲
Warpage ≤2.0 mm
热重分析（5%损失）
TGA ＞300℃
剥离强度（after PCT）
Peel strength ＞30N/cm
固化条件：180-220℃×5-10min or 110-150℃×20-30min Curable condition：180-220℃×5-10min or 110-150℃×20-30min
X-BC电池专用绝缘胶
Insulation layer for X-BC Photovoltaic Cell
10
热固绝缘胶（透明色）
Heat curable insulation layer/（Clear）
指标 Requirement 结果 Result
绝缘性
Insulation resistance ≥1×10 Ω
体积电阻
Volume resistivity ≥1×10 Ω.cm 13
击穿强度
Dielectric strength ≥15kV/mm
有机扩散
Organic spread ＜10%
有机浸润
Organic infiltration ＜200um
耐湿热性能
DH1000 pass
耐冷热冲击
TC200 pass
高压蒸煮试验
PCT 96hours
固化后硬度
Pencil hardness ≥5H
高温后翘曲
Warpage ≤2.0 mm
热重分析（5%损失）
TGA ＞300℃
剥离强度（after PCT）
Peel strength ＞30N/cm
固化条件：180-220℃×5-10min or 110-150℃×20-30min Curable condition：180-220℃×5-10min or 110-150℃×20-30min
X-BC电池专用绝缘胶
Insulation layer for X-BC Photovoltaic Cell
10
耐紫外老化性能（120kWh/m2）
QUV Δb ≤3
适用于单双玻组件
For single/double side module
高紫外透过率
High UV transmittance
适合丝网印刷
For screen print
良好的印刷特性，塑形佳，宽泛的操作窗口
Good printing characteristics & shaping， wide processing window
优异的绝缘性、耐PCT性
Excellent insulation performance & PCT resistance
与胶膜粘接力强
High peel strength with encapsulation film
UV绝缘胶（绿色）
UV curable insulation layer/（Green）
指标 Requirement 结果 Result
绝缘性
Insulation resistance ≥1×10 Ω
体积电阻
Volume resistivity ≥1×10 Ω.cm 13
击穿强度
Dielectric strength ≥15kV/mm
有机扩散
Organic spread ＜10%
有机浸润
Organic infiltration ＜100um
耐湿热性能
DH1000 pass
耐冷热冲击
TC200 pass
高压蒸煮试验
PCT 96hours
固化后硬度
Pencil hardness ≥4H
高温后翘曲
Warpage ≤1.0 mm
热重分析（5%损失）
TGA ＞300℃
剥离强度（after PCT）
Peel strength ＞30N/cm
固化条件：10000-20000mJ/cm² Curable condition：10000-20000mJ/cm²
X-BC电池专用绝缘胶
Insulation layer for X-BC Photovoltaic Cell
10
适合丝网印刷
For screen print
良好的印刷特性，塑形佳，宽泛的操作窗口
Good printing characteristics & shaping，
wide processing window
紫外线固化（汞灯或LED）
UV curable（mercury lamp or LED）
优异的绝缘性、耐PCT性
Excellent insulation performance & PCT resistance
与胶膜粘接力强
High peel strength with encapsulation film
UV绝缘胶（透明色）
UV curable insulation layer/（Clear）
指标 Requirement 结果 Result
绝缘性
Insulation resistance ≥1×10 Ω
体积电阻
Volume resistivity ≥1×10 Ω.cm 13
击穿强度
Dielectric strength ≥15kV/mm
有机扩散
Organic spread ＜10%
有机浸润
Organic infiltration ＜100um
耐湿热性能
DH1000 pass
耐冷热冲击
TC200 pass
高压蒸煮试验
PCT 96hours
固化后硬度
Pencil hardness ≥4H
高温后翘曲
Warpage ≤1.0 mm
热重分析（5%损失）
TGA ＞300℃
剥离强度（after PCT）
Peel strength ＞30N/cm
固化条件：10000-20000mJ/cm² Curable condition：10000-20000mJ/cm²
X-BC电池专用绝缘胶
Insulation layer for X-BC Photovoltaic Cell
10
耐紫外老化性能（120kWh/m2）
QUV Δb ≤3
适用于单双玻组件
For single/double side module
高紫外透过率
High UV transmittance
良好的印刷特性，塑形佳，宽泛的操作窗口
Good printing characteristics & shaping, wide processing window
紫外线固化（汞灯或LED）
UV curable（mercury lamp or LED）
优异的绝缘性、耐PCT性
Excellent insulation performance & PCT resistance
与胶膜粘接力强
High peel strength with encapsulation film
适合丝网印刷
For screen print
感光胶
Liquid plating resist
指标 Requirement 结果 Result
涂布方式
Coating 丝网印刷 Screen printing
粘度
Viscosity 1500-3000cps
干膜厚度
Thickness 10-15um
干燥条件
Tack dry 75℃-90℃×10-5min
侧蚀
Under-cut ＜5um
卤素
Halogen Halogen free
感光性
Photosensitivity LDI,405nm, 60-100mJ/cm²,
解析度
Resolution ≤20um
正面保护胶
Isolation layer
指标 Requirement 结果 Result
涂布方式
Coating 丝网印刷 Screen printing
粘度
Viscosity 15000-30000cps
干膜厚度
Thickness 10-15um
干燥条件
Tack dry
热固化：75℃-90℃×10-5min
透光度
Transmittance ＞90%
热黄变
（200℃×30min） Δ b＜2
UV固化：10000-30000mJ/cm